Low alloy tool steel bar, mat number 1.2210
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-10-02 16:27
- Browse the number:
120
Company Profile
- GENPHOAL TECHNOLOGY(B.V.I.)CO., LTD
-
Contact:
bozhong(Ms.)
-
Telephone:
-
Area:
Beijing
-
Address:
Lingdinghu Industrial Zone, Luoyang, Town, Boluo County, Huizhou City, Guangdong Province. China, Huizhou, Guangdong, China (516000)
- Website: http://bozhong.alxstewartagriculture.com/
By certification [File Integrity]
Product details
Model Number: ZXL045
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steelApplicationsSpiral and tap drills, broaching tools, engraving tools, ejectors, metal sawsChemical composition (in weight%)C 1.17
Si 0.23
Mn 0.30
Cr 0.65
V 0.10
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Thermal conductivity [W/m. K]: 33.5, 32(500℃), 31(700℃)
Electric resistivity [Ohm mm2/m]: 0.33
Specific heat capacity [J/g. K]: 0.46
Soft annealing
Heat to 710-850℃, cool slowly in furnace
This will produce a maximum Brinell hardness of 223
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650℃, holding for 1hour at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden froma temperature of 780-820℃, 800-840°C followed by oil or water quenching
Hardness after quenching is 64-66 HRC
Tempering
Tempering temperature: 100-400°C
Forging
Hot forming temperature: 1050-850°C
Corrosion resistance
This is an alloy steel and it is not corrosion resistant
Will rust unless protected
Specifications:
Grade: mat number 1.2210
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy packing or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Si 0.23
Mn 0.30
Cr 0.65
V 0.10
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Thermal conductivity [W/m. K]: 33.5, 32(500℃), 31(700℃)
Electric resistivity [Ohm mm2/m]: 0.33
Specific heat capacity [J/g. K]: 0.46
Soft annealing
Heat to 710-850℃, cool slowly in furnace
This will produce a maximum Brinell hardness of 223
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650℃, holding for 1hour at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden froma temperature of 780-820℃, 800-840°C followed by oil or water quenching
Hardness after quenching is 64-66 HRC
Tempering
Tempering temperature: 100-400°C
Forging
Hot forming temperature: 1050-850°C
Corrosion resistance
This is an alloy steel and it is not corrosion resistant
Will rust unless protected
Specifications:
Grade: mat number 1.2210
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy packing or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Dishwashers Descaler
price: Negotiable
-
AISI 304 Stainless Steel Castings
price: Negotiable
-
Extreme Cushioning Flyknit Safety Shoes
price: Negotiable
-
3oz Hot Coffee Paper Cup
price: Negotiable
-
Air Cooled Condensing Unit with Scroll Compressor
price: Negotiable
-
Wheeled Bulk Reception Feeder
price: Negotiable